C36300

Home > Metal > Leaded Brass > C36300

Equivalent Specification

Symbol	UNS	EN	BS	JIS	IS
CuZn37	C36300	-	-	-	-

Chemical Composition

Elements	Min (%)	Max (%)
Cu	61.0	63.0
Pb	0.25	0.7
Fe	-	0.15
P	0.04	0.15
Total Imp	-	0.5
Zn	Remainder

Mechanical Properties According To ASTM B921 (As Per Temper HO2)

Range (Inch)	Form	To	UTS Min (Ksi)	PS Min (Ksi)	ELo Min (%)	Hardness Min (HRB)	Hardness Max (HRB)
Round (Dia)	0.059	0.5	63	28	10	-	-
	0.5	1	55	26	12	-	-
	1	2	48	24	20	-	-
	2	2.9527	45	20	25	-	-
Hex (A/F)	0.1181	0.5	63	28	10	-	-
	0.5	1	55	26	12	-	-
	1	2	48	24	20	-	-
	2	2.7559	45	20	25	-	-
Square (A/F)	0.1181	0.5	63	28	10	-	-
	0.5	1	55	26	12	-	-
	1	2	48	24	20	-	-
	2	2.3622	45	20	25	-	-
Rectangle (Thickness)	0.1181	0.5	63	28	10	-	-
	0.5	1	55	26	12	-	-
	1	1.9685	48	24	20	-	-

Range (MM)	Form	To	UTS Min (Mpa)	PS Min (Mpa)	ELo Min (%)	Hardness Min (HRB)	Hardness Max (HRB)
Round (Dia)	1.5	12	430	190	10	-	-
	12	25	380	180	12	-	-
	25	50	330	165	20	-	-
	50	75	310	135	25	-	-
Hex (A/F)	3	12	430	190	10	-	-
	12	25	380	180	12	-	-
	25	50	330	165	20	-	-
	50	70	310	135	25	-	-
Square (A/F)	3	12	430	190	10	-	-
	12	25	380	180	12	-	-
	25	50	330	165	20	-	-
	50	70	310	135	25	-	-
Rectangle (Thickness)	3	12	430	190	10	-	-
	12	25	380	180	12	-	-
	25	50	330	165	20	-	-

Physical Properties

Melting Point - Liquidus °F	1650
Melting Point - Solidus °F	1630
Density lb/cu in. at 68 °F	0.304
Specific Gravity	8.42
Electrical Conductivity %IACS at 68 °F	26
Thermal Conductivity Btu/ sq ft/ ft hr/ °F at 68 °F	51.5
Specific Heat Capacity Btu/ lb / °F at 68 F	0.088

Fabrication Properties

Melting Point - Liquidus °F	1650
Melting Point - Solidus °F	1630
Density lb/cu in. at 68 °F	0.304
Specific Gravity	8.42
Electrical Conductivity %IACS at 68 °F	26
Thermal Conductivity Btu/ sq ft/ ft hr/ °F at 68 °F	51.5
Specific Heat Capacity Btu/ lb / °F at 68 F	0.088

Typical Uses

Plumbing