| Elements |
Min (%) |
Max (%) |
| Cu |
57.00 |
59.00 |
| Al |
- |
0.05 |
| Fe |
- |
0.30 |
| Ni |
- |
0.30 |
| Pb |
1.60 |
2.50 |
| Sn |
- |
0.30 |
| Total Others |
- |
0.20 |
| Zn |
Remainder |
Mechanical Properties According To EN12164 (As Per Temper R430)
| Range (mm) |
From |
To |
UTS Min (N/mm²) |
PS Min (N/mm²) |
Elongation Min (%) |
Hardness Min (HV) |
Hardness Max (HV) |
| Round (Dia) |
2 |
40 |
430 |
220 |
10 |
- |
- |
| Hex (A/F) |
2 |
35 |
430 |
220 |
10 |
- |
- |
| Square (A/F) |
2 |
35 |
430 |
220 |
10 |
- |
- |
| Rectangle (Thickness) |
3 |
40 |
430 |
220 |
10 |
- |
- |
| PHYSICAL PROPERTIES |
| Physical Properties |
Metric |
English |
| Density |
8.40 g/cc |
0.303 lb/in3 |
| CTE, linear |
26.0 ᶙm/m-˚C |
14.4 ᶙin/in-˚F |
| Specific Heat Capacity |
0.380 J/g-˚C |
0.0908 BTU/lb-˚F |
| Thermal Conductivity |
113 W/m-K |
784 BTU-in/hr-ft²-˚F |
| Melting Point |
880-900 ˚C |
1620 – 1650 ˚F |
| Solidus |
880 ˚C |
1620 ˚F |
| Liquidus |
900 ˚C |
1650˚F |
| FABRICATION PROPERTIES |
| Forming |
Suitability |
| Machinability (CuZn39Pb3 = 100 %) |
95.00% |
| Capacity for Being Cold Worked |
Poor |
| Capacity for Being Hot Worked |
Excellent |